11. STAVAX Mold wire
This welding wire welding advanced stainless steel, corrosion resistance, high wear resistance and good polishing.
Hardness: 33-36HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0 mm
ingredient: C:0.25 | MN:0.50 | SI:0.90 | CR:12 |
MO:0.35 | V:0.30 | NI:1.30 |
12. 2344 Mold wire
Has excellent machinability and polishability, excellent overall hardening, good high temperature strength, heat very low deformation of the treatment, good quenching, specializing in pressure hot work die steel.
Hardness: 52-55HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.35-0.45 | MN:0.45-0.55 | SI:2.10-3.50 | CR:9-12 |
MO:1.0-1.30 | V:0.4 | W:1.20 |
13. 2083 Mold wire
The wire with high CR anti-acid, after quenching better wear resistance, suitable for electric erosion operation, suitable for acidic plastic.As well as the need for good polishing of the mold.
Hardness: 31-34HRC
Specifications: 0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.25-0.40 | MN:0.50-0.60 | SI:0.40-0.50 | CR:12-14 |
MO:0.70-0.80 | N:0.50-0.65 | P:0.20 | CU:0.65-0.75 |
14. H13 Mold wire
Dedicated to welding hot work steel series of steel, precision forging die, hot die, aluminum die-casting mold, with good heat resistance and resistance to cracking, the welding wire after welding the original color of the base material, hardness enough.
Hardness: 53-57HRC
Specifications: 0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.35-0.45 | MN:0.25-0.45 | SI:0.85-1.25 | P:0.20-0.30 |
MO:1.0-1.50 | CR:5-8 | S:0.20-0.30 | V:0.80-1.10 |
15. 2311 Mold wire
Suitable for chrome surface treatment, uniform material, good machinability, nitriding treatment, the organization for the shellfish Di body.
Hardness:35-38HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.35-0.40 | MN:1.30-1.50 | SI:0.30-0.40 | CR:1.80-2.0 |
MO:0.15-0.25 | S:0.005 | NI:0.40 |
16. Copper alloy welding wire
An alloy of one or more elements is added to pure copper, and the pure copper density is 8.50 m.For the 1083C, with excellent conductivity, thermal conductivity, commonly used in heat exchangers, pipes, transformers Etc ... thermal equipment.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
17. Brass welding wire
Brass is made of copper and zinc alloy, often used in the manufacture of valves, water pipes, air conditioning inside and outside the machine, watches and clocks, connecting pipes and radiators, about 60% copper containing about 40%
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.0 mm
18. DC53 welding wire
Welding hot work die steel, heat shock cracking, thermal wear, unique performance often become a repair die casting Mold, hot forging, hot extrusion die steel up to the choice.
Hardness:51--53HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.28-0.35 | MN:0.40-0.50 | SI:0.80-1.00 | CR:5-6 |
MO:2.0-2.50 | V:0.60-0.80 |
19. Leather copper mold wire
Copper alloy for welding electrolytic film, copper, copper and several different types of metal bonding, the market is generally used in welding shoe mold, copper cups, copper casting connection, hot runner cooling system and other purposes. Is a good combination of mechanical properties, chemical properties and corrosion resistance of non-ferrous metals, aging treatment with a special steel with a high hardness limit, while With a high conductivity, thermal conductivity and wear resistance, hardness of 36-42 softening temperature of 930, due to copper welding will release harmful substances, welding should be done when the protection.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
20. SKH-9 mold welding wire
Welding high-speed steel series alloy tool steel, high hardness tool hard surface production welding, knife edge, blade, blade 、Cut mouth, jaw position, high wear resistance and other parts.
Hardness:61-63HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm