21. 45C mold wire
This wire is a medium carbon steel structure, hot and cold processing performance are good, good mechanical properties, and the price low so widely used, but the quenching through the low, requiring high workpiece, mold should not be used.
Hardness:29-31HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.30-0.45 | MN:0.40-0.55 | SI:0.35 | CR:0.25-0.35 |
S:0.025-0.040 | P:0.035 | NI:0.25-0.35 |
22. 55C Mold wire
This wire is a high-strength medium carbon steel, hot and cold processing performance are appropriate, easy cutting, after treatment.The surface has a higher hardness and tension, but the plastic, poor quenching, used in dynamic load and impact load not big workpieces.
Hardness: 29-34HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.35-0.55 | MN:0.50-0.70 | SI:0.35 | CR:0.35-0.45 |
S:0.025-0.040 | P:0.035 | NI:0.25-0.35 | CU:0.20 |
23. 2316 Mold wire
Suitable for plastic mold commonly used mirror mold steel, with excellent corrosion resistance, high polishing,Organization uniform, comprehensive good.
Hardness: 34--38HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.40-0.50 | MN:0.5-0.60 | SI:0.80-0.90 | CR:10-12 |
MO:0.20-0.35 |
24. 308L stainless steel welding wire
Dedicated to welding stainless steel products, parts, etc., its characteristics, good crack resistance, good corrosion resistance, low carbon ,after welding bright, no rust, no yellow, good mobility
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
25. 316L Stainless steel welding wire
Dedicated to the need for anti-acetic acid, anti-sulfurous acid, anti-phosphoric acid, and salt wear-resistant stainless steel, suitable for food,Class processing equipment of stainless steel and medical equipment products.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0 mm
26. Special stainless steel welding wire
Special stainless steel is different from general stainless steel, which is characterized by austenitic stainless steel, characterized by high nickel,High chromium, high molybdenum, high alloy has a more excellent corrosive, not the general stainless steel can replace.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
27. Aluminum-magnesium welding wire
Is a magnesium containing 5% of the aluminum alloy filled with metal, has a good resistance to seawater corrosion, in the anode after treatment of the color is white, tensile strength of 290MP.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
28. Aluminum silicon welding wire
Is a silicon-containing 5% aluminum-silicon alloy filled metal, melting point temperature range of 1065-1170F, anode after treatment, the color is gray and the minimum tensile strength is 186MP.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
29. Aluminum-zinc welding wire
Is a zinc-containing alloy filled with metal, the melting point temperature range of 1070-1080F, after the anodized color for gray and black. Can be welded 6061 6053
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
30. Aluminum manganese welding wire
Is a manganese-containing aluminum alloy filled metal, the melting point of the temperature range of 1065-1075F, after anodized Yan Color is black. Can be welded 7005 7100 3003 3004
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm