22. 888 mold welding wire
The welding wire for the high-strength welding wire, easy to repair easy to crack tool steel, commonly used in explosion-proof, filling the bottom of the welding again, Rally strong, greatly reduced after welding cracked the phenomenon.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
23. CR12MOV mold welding wire
Special repair complex with high-carbon high-chromium cold-working die steel, belonging to the column metal, has a high hardenability, hardening and resistance Grinding, quenching deformation less, but not ideal is its thermal conductivity, high temperature plasticity, impact toughness is poor.
Hardness: 52--56HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:2.00-2.50 | MN:0.35-0.45 | SI:0.30-0.40 | CR:11-13 |
P:0.020-0.035 | S:0.025-0.030 |
24. Nitriding welding wire
Dedicated to a variety of nitriding die steel, good weld fit, beautiful color, anti-cracking strong, is very good Use wire.
25. Titanium welding wire
Is an important structural metal, with high strength, good corrosion resistance, high heat resistance and is widely used in various lines Industry, mainly for the aviation industry.
26. HSS High speed steel welding wire
Is a complex composition of alloy steel, containing tungsten, molybdenum, chromium, vanadium and other elements, it is produced in high-speed cutting
High heat conditions can still maintain a high hardness, HRC can be more than 60 degrees, but the processing process is more complex, Must be annealed, quenched, tempered and a series of processes, commonly used in the manufacture of various cutting tools, such as turning tools, drilling Head, hob, machine saw blade and the requirements of high mold.
Hardness: 61-63HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6 mm
27. Nickel welding wire
Nickel its resistance to alkaline corrosion in the metal material after silver, nickel in the concentrated alkali surface will generate a layer of black of the protective film, it is very resistant to corrosion, with a high surface quality, processing performance, high melting point, easy to degrease, commonly used
In the production of such as anodes, septa, electronic stent, etc., is an important material in vacuum electronic devices.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
28. MASIC mold welding wire
This product is special welded martensitic aging steel series, precision plastic mold, precision aluminum die-casting mold, mirror processing and excellent erosion, aging treatment after 3 hours to reach 49-52HRC with high hardness, temperature and anti-wear effectively extend the mold life
29. 2738 mold welding wire
Mainly used for the processing of plastic mold production, pre-hardness is good, processing and strong, suitable for high-light finish of the mold
Such as PS, ABS, commonly used in TV shell mold, fax machines
Hardness: 33-38HRC
Specifications: 0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.35-0.40 | MN:0.9-1.10 | NO:0.35-0.45 | CR:0.20-2.30 |
NI:1.0-1.20 |
30. M2 mold welding wire
Suitable for repair precision work High-speed production stamping die, after welding with wear resistance, high toughness, high compressive strength
In the repair tool industry occupies a very important position.
Hardness: 62-65HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:0.9-1.0 | MN:0.7-1.0 | P:0.035 | CR:17-20 |
NI:0.025 | SI:0.20-0.35 | S:0.030 | MO:0.08-1.10 |
31. M333 mold welding wire
Suitable for acidic corrosive plastic mold, with a high degree of mirror finish, excellent thermal conductivity than the general heat better, more corrosion resistance, so that the mirror to maintain the best long-term status.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
32. D2 mold welding wire
This wire is used for complex and possible deformation of the tool steel, high wear resistance of the long life of various types of cold mold and cold cutting edge
Cold extrusion die, stretch die, the general use of D2 material prone to fatigue fracture, the use of this wire can reduce the fracture.
Hardness: 47-52HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
ingredient: C:1.5-1.80 | MN:0.40-0.60 | SI:0.50-0.80 | P:0.03-0.04 |
MO:1.0-1.20 | CR:12-13.50 | S:0.03-0.04 | V:0.80-1.10 |
33. 310 mold welding wire
The main welding needs high temperature conditions of the metal structure, for welding a small area of glass mold boiler liner, heat treatment equipment has a good anti-high temperature effect, can be welded 310 314 410 430 502 high temperature stainless steel.
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm
34. 935 steel welding wire
The welding wire is a carbon-manganese alloy wire, it can be completely consistent with the heat treatment of steel and other procedures of the hardness changes, specifically for welding welding angle position when the effect is better, can be welded steel base metal mold, including K-460 DF2 And so on Steel.
Hardness: 50--52HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
35. Ace welding wire
This wire is used to weld the requirements of the mold is not high, good flow of welding, sand holes less, strong pull, no residue after welding, hardness Moderate, easy to facilitate milling, polished and easy to clean color and other steel match, greatly reduce the yin and yang phenomenon.
36. Copper welding wire
Widely used copper alloy welding wire, welding electrolytic film, iron, copper, steel, or two different types of metal bonding, generally applicable welding shoe mold, mold change water plug hole, copper casting connection and other purposes.
37. 1.2343 mold welding wire
After welding this wire has a good hardenability, ductility, stability in all directions, mainly used in die-casting mold (Mold core mold split cone, etc ..) aluminum copper and magnesium hot forming die, cold mold, trimming, thermal shear, tightening and Wearable parts used.
Hardness: 42-50HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.20-0.30 | MN:0.40-0.50 | SI:0.50-0.80 | CR:7-9 |
MO:1.0-1.20 | V:0.9 |
38. 1.2344 mold welding wire
Dedicated to repair pressure with a thermal die, cold die, after welding material uniform, the effect is ideal, with a very good Good polishing performance, low temperature wear resistance, high temperature fatigue and heat resistance. Commonly used in the use of wear parts.
Hardness: 42-50HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.25-0.35 | MN:0.40-0.50 | SI:0.55-0.90 | CR:8-10 |
MO:1.2-1.50 | V:0.9 |
39. FDAC mold welding wire
This wire is dedicated to aluminum-zinc-magnesium alloy die-casting mold, high-hard plastic mold, extrusion mold, with re-processing.Easy to perform excellent, wear and high temperature, wide range of uses.
Hardness: 40-48HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4/3.2 mm
ingredient: C:0.30-0.38 | MN:0.50-0.60 | SI:0.7-0.85 | CR:5-7 |
MO:1.10-1.50 | V:0.7 | S:0.13 | P:0.030 |
40. 420 mold welding wire
Applicable to all kinds of plastic high-mirror mold, or have special requirements of the mold, corrosion resistance, good wear resistance after the long-term use of the mold after the surface can still maintain the original smooth state, the mold in a humid environment or storage does not need Special protection, processing costs affordable.
Hardness: 38-43HRC
Specifications:0.2/0.3/0.4/0.5/0.6/0.8/0.9/1.0/1.2/1.6/2.0/2.4 mm